新型牙科复合树脂的制备与机械性能研究

李迪1, 李保泉1, 魏玉雪3, 牛菊1, 赵文迪1, 刘丹丹1, 那辉2, 刘晓秋1*   

  1. 1. 吉林大学口腔医学院修复科 吉林 长春 130021;
    2. 吉林大学化学院 吉林 长春 130021;
    3. 乌鲁木齐市国际医院口腔修复科 新疆 乌鲁木齐 830091
  • 收稿日期:2018-04-04 出版日期:2018-11-28 发布日期:2018-11-23
  • 通讯作者: 刘晓秋,电话:0431-88796018
  • 作者简介:李迪(1990~ ),女,吉林人,硕士,主要从事口腔修复学方面的研究。
  • 基金资助:
    国家自然科学基金(编号:813711841014238);吉林省科技厅资助项目(编号:20160519017JH)

Preparation and Mechanical Properties of New Dental Composite Resin

LI Di1, LI Bao-quan1, WEI Yu-xue3, NIU Ju1, ZHAO Wen-di1, LIU Dan-dan1, NA Hui2, LIU Xiao-qiu1*   

  1. 1. Department of Rehabilitation, Stomatological Hospital, Jilin University, Changchun 130021, China;
    2. College of Chemistry, Jilin University, Changchun 130021, China;
    3. Department of Rehabilitation, International Hospital of Urumqi, Urumqi 830091, China.
  • Received:2018-04-04 Online:2018-11-28 Published:2018-11-23

摘要: 目的:研究纳米/微米SiO2混合填料对新型牙科复合树脂机械性能的影响。方法:将纳米/微米SiO2混合填料加入联苯基单体TMBPEA中,制备新型牙科复合树脂。实验分为5个实验组和1个以Bis-GMA为单体的对照组,测试各组试样的挠曲强度、弹性模量;扫描电镜观察含SiO2填料样本的断面形貌。结果:含TMBPEA和50%SiO2填料组试样的机械性能最高,挠曲强度和弹性模量分别为(96.83±0.55) MPa、(7.12±0.20) GPa。SEM结果显示该组试样的无机填料均匀致密地分散在连续的有机基质中。结论:以TMBPEA为基质的复合树脂是一种有应用前景的牙科复合树脂材料。

关键词: 联苯, 牙科复合树脂, SiO2无机填料, 机械性能, 显微形貌

Abstract: Objective: To evaluate the effect of nanometer/micron SiO2 mixed filler on mechanical properties of a new type of dental composite resin. Methods: A new type of dental composite resin was prepared by adding nanometer/micron SiO2 mixed packing to monomer of TMBPEA. The experiment was divided into five experimental groups and one control group with Bis-GMA as the monomer, and the flexural strength and elastic modulus of each group were tested. The section morphology of samples containing SiO2 fillers were observed by SEM. Results: The mechanical properties of the samples with TMBPEA and 50% SiO2 filler were the highest. Its bending strength and elastic modulus were (96.83+0.55) MPa and (7.12±0.20) GPa, respectively. SEM results showed that the inorganic filler of the sample was dispersed uniformly in the continuous organic matrix. Conclusion: The composite resin with TMBPEA as matrix has promising application prospect.

Key words: Biphenyl, Dental composites resins, SiO2 inorganic filler, Mechanical property, Mixed system