染色和遮色处理对氧化锆与树脂粘接性能的影响

doi:10.13701/j.cnki.kqyxyj.2020.06.021

口腔医学研究 ›› 2020, Vol. 36 ›› Issue (6): 595-598.DOI: 10.13701/j.cnki.kqyxyj.2020.06.021

染色和遮色处理对氧化锆与树脂粘接性能的影响

高楠¹, 韦羽和², 姜潇², 路炜^1*

1.山东省立医院口腔科山东济南 250021;
2.山东大学口腔医学院山东济南 250012

收稿日期:2019-12-31 出版日期:2020-07-03 发布日期:2020-07-06
通讯作者: ^*路炜,E-mail:luwei.510@163.com
作者简介:高楠(1987~ ),女,山东新泰人,硕士,医师,主要从事口腔修复学及材料学研究。

Effect of Masking Treatment on Structure Surface on Adhesion Properties between Zirconia and Resin

GAO Nan¹, WEI Yuhe², JIANG Xiao², LU Wei^1*

1. Department of Stomatology, Shandong Provincial Hospital, Jinan 250021, China;
2. School of Stomatology, Shandong University, Jinan 250012, China

Received:2019-12-31 Online:2020-07-03 Published:2020-07-06

摘要/Abstract

摘要： 目的: 探讨组织面遮色处理对氧化锆与树脂间粘接性能的影响。方法: 制作氧化锆试件并随机分为3组:对照组、浸泡染色组、浸泡染色遮色组。每组随机分为2个亚组,分别涂或不涂硅烷耦联剂。测试3组试件接触角;将试件与树脂水门汀粘接,24 h后进行剪切粘接强度测试并观察界面断裂模式。结果: 各组接触角,断裂模式无统计学差异;浸染组粘接强度与对照组无统计学差异,浸染并遮色组粘接强度显著低于对照组及浸染组;各硅烷耦联剂亚组粘接强度显著高于不涂组。结论: 浸泡染色对氧化锆陶瓷与树脂间粘接强度无显著影响;浸染后遮色处理可降低氧化锆陶瓷与树脂间粘接强度;涂布硅烷耦联剂可显著增强氧化锆陶瓷与树脂间粘接强度。

关键词: 浸泡染色, 遮色处理, 氧化锆陶瓷, 粘接强度

Abstract: Objective: To investigate the effect of masking treatment on the adhesion between zirconia ceramics and resin. Methods: Zirconia specimens were made and randomly divided into 3 groups: control group, immersion dyeing group, and immersion dyeing masking group. Each group was randomly divided into 2 subgroups, with or without silane coupling agent. The contact angles of specimens were tested. The specimens were bonded with the resin cement. The shear bond strength was tested after 24 hours and the interface fracture mode was observed. Results: There was no statistical difference in contact angle and fracture mode between the groups. There was no difference in the bonding strength between the immersion dyeing group and the control group. The bonding strength of the immersion dyeing-masking group was significantly lower than those of other two groups. Subgroups coated with a silane coupling agent had significantly higher bonding strength than those without coating. Conclusion: The immersion dyeing has no significant effect on the bonding strength between zirconia ceramics and resins. The masking treatment after immersion dyeing can reduce the bonding strength between zirconia ceramics and resins. Coating silane coupling agents can significantly enhance the zirconia ceramics and resins bonding strength.

Key words: immersion dyeing, masking treatment, shear bond strength, zirconia

高楠, 韦羽和, 姜潇, 路炜. 染色和遮色处理对氧化锆与树脂粘接性能的影响[J]. 口腔医学研究, 2020, 36(6): 595-598.

GAO Nan, WEI Yuhe, JIANG Xiao, LU Wei. Effect of Masking Treatment on Structure Surface on Adhesion Properties between Zirconia and Resin[J]. Journal of Oral Science Research, 2020, 36(6): 595-598.

参考文献

[1] 周愚非,李清.两种不同通透率Nacera氧化锆的色度学研究[J].口腔医学研究,2018,34(8):889-892.
[2] 爱迪特(秦皇岛)科技股份有限公司.一种牙科氧化锆陶瓷用遮色液及其制备方法和应用:CN201810974678.8[P].2018-12-28.
[3] 冯靓婧,于皓,程辉.烧结次数对不同方法染色的氧化锆陶瓷粘接性能的影响[J].口腔医学研究,2018,34(2):172-175.
[4] 刘小丽,廖岚.牙科用氧化锆陶瓷材料着色的研究进展[J].现代诊断与治疗,2019,30(1):48-52.
[5] 石连水.3Y-TZP基牙科陶瓷的颜色和荧光调控[D].江西:南昌大学,2015.
[6] Kim MJ, Oh SH, Kim JH,et al. Wear evaluation of the human enamel opposing different Y-TZP dental ceramics and other porcelains[J].J Dent, 2012, 40(11):979-988.
[7] Mahshid M,Berijani N,Sadr SJ,et al. Effect of coloring-by-dipping on microtensile bond strength of zirconia to resin cement [J]. J Dent (Tehran), 2015, 12(6):414-423.
[8] Kim GH,Park SW,Lee K,et al. Shear bond strength between resin cement、and colored zirconia made with metal chlorides [J]. J Prosthet Dent,2015,113(6):603-608.
[9] 崔新悦,佟岱,王新知,等.对比切削与胶态成型工艺制作的氧化锆陶瓷的透光性与遮色效果[J].北京大学学报(医学版),2018,50(1):85-90.
[10] Shiraishi T, Watanabe I. Thickness dependence of light transmittance, translucency and opalescence of a ceria-stabilized zirconia/alumina nanocomposite for dental applications [J]. Dent Mater, 2016,32(5):660-667.
[11] 黄沈涛.可切削陶瓷内层涂层对粘接强度的影响[D].北京:首都医科大学,2013.
[12] Khan AA, Al Kheraif AA, Jamaluddin S, et al. Recent trends in surface treatment methods for bonding composite cement to zirconia: a reveiw [J]. J Adhes Dent,2017,19(1):7-19.
[13] Nguyen TPT , Oh GJ , Lim HP , et al. Evaluation of sandblasting on mechanical properties and cell response of bioactive glass infiltrated zirconia[J]. J Nanosci Nanotechnol, 2017, 17(4):2740-2742.
[14] Liu D, Tsoi KH, Matinlinna JP, et al. Effects of some chemical surface modifications on resin zirconia adhesion [J]. J Mech Behav Biomed Mater, 2015, 46:23-30.
[15] Cakirbay TM, Cihan A. Effects of different surface treatment methods and MDP monomer on resin cementation of zirconia ceramics an in vitro study [J]. J Lasers Med Sci, 2015, 6(4):174-181.
[16] Thammajaruk P, Buranadham S, Thanatvarakorn O, et al. Influence of glass-ceramic coating on composite zirconia bonding and its characterization [J]. Dent Mater, 2019, 35(1):105-113.

染色和遮色处理对氧化锆与树脂粘接性能的影响

Effect of Masking Treatment on Structure Surface on Adhesion Properties between Zirconia and Resin

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 13

编辑推荐

Metrics

[1]	王雯, 谢翠柳, 邓婷, 刘雯, 刘敏. 原花青素对纤维桩粘接耐久性的影响[J]. 口腔医学研究, 2020, 36(3): 216-220.
[2]	邓婷, 刘敏, 刘雯, 王雯, 谢翠柳. EDTA和EDC预处理对两步法自酸蚀粘接剂粘接强度的影响[J]. 口腔医学研究, 2020, 36(3): 221-225.
[3]	王美艳, 赵婵媛, 王杨洋, 王熙. 不同抛光处理对两种氧化锆陶瓷表面粗糙度和细菌粘附性能的影响[J]. 口腔医学研究, 2020, 36(3): 239-242.
[4]	李秀花, 于鹏, 田福聪, 王晓燕. 磷酸预处理对两步法自酸蚀粘接剂与牙釉质粘接强度的影响[J]. 口腔医学研究, 2019, 35(8): 748-751.
[5]	尹路, 郑燕芬. 预备与不预备前牙超薄瓷贴面断裂模式的比较研究[J]. 口腔医学研究, 2019, 35(4): 382-385.
[6]	冯靓婧, 于皓, 程辉. 烧结次数对不同方法染色的氧化锆陶瓷粘接性能的影响[J]. 口腔医学研究, 2018, 34(2): 172-175.
[7]	卢冠凡,冯琨,苏征,纪海. Nd:YAG根管荡洗技术对纤维桩粘接效果的影响[J]. 口腔医学研究, 2018, 34(12): 1320-1323.
[8]	李欣霖,韩汉,谢金玲,吴佩玲. RMGIC联合自酸蚀粘接剂修复Ⅴ类洞粘接强度和边缘微渗漏的研究[J]. 口腔医学研究, 2017, 33(12): 1282-1285.
[9]	吕林虎,周会,黎佳灵,郭玲. 磷酸浓度对氟斑牙牙釉质微拉伸粘接强度影响的研究[J]. 口腔医学研究, 2017, 33(1): 51-54.
[10]	甘婧,刘思颖,姚陈敏,黄翠. 不同能量密度Nd:YAG激光照射对牙本质粘接强度的影响[J]. 口腔医学研究, 2016, 32(4): 356-360.
[11]	林婷婷,樊江源,郑瑞斌,王思钱,胡方旋,麻健丰. 光纤激光蚀刻对氧化锆陶瓷性能影响的研究[J]. 口腔医学研究, 2016, 32(1): 12-16.
[12]	邵方洋, 杨晓烨, 姜慧茜, 樊江源, 周巧玲, 谷锦超, 郑铁丽. 丙酮基和酒精-水基牙本质粘接系统粘接强度比较及粘接界面观察[J]. 口腔医学研究, 2015, 31(3): 272-275.
[13]	任青杰,王迎捷,张翔,徐宏宇,安佰利,陈吉华. 不同激活剂对长链硅烷偶联效能影响的研究[J]. 口腔医学研究, 2015, 31(2): 101-104.