Development of Glass Ionomer Cement Modified by Nano-fillers

doi:10.13701/j.cnki.kqyxyj.2022.01.003

Abstract

Abstract: Glass ionomer cement (GIC) has been universally used for tooth restoration. However, its insufficient antibacterial and mechanical properties usually lead to damage and secondary caries, resulting in the treatment failure. With the development of material technology, nano particle came into existence and has been utilized in the modification of GIC due to its excellent properties. However, current studies are still imperfect. Here, the researches on GIC modified by different nano-fillers are systematically reviewed.

Key words: nano-filler, glass ionomer cement, modification, research

ZHU Keshi, REN Liling. Development of Glass Ionomer Cement Modified by Nano-fillers[J]. Journal of Oral Science Research, 2022, 38(1): 13-16.

References

[1] Ruengrungsom C, Palamara J, Burrow M. Comparison of ART and conventional techniques on clinical performance of glass-ionomer cement restorations in load bearing areas of permanent and primary dentitions: A systematic review[J]. J Dent, 2018, 78:1-21.
[2] Farrugia C, Camilleri J. Antimicrobial properties of conventional restorative filling materials and advances in antimicrobial properties of composite resins and glass ionomer cements-A literature review [J]. Dent Mater, 2015, 31(4):e89-e99.
[3] Paiva L, Fidalgo TKS, da Costa LP, et al. Antibacterial properties and compressive strength of new one-step preparation silver nanoparticles in glass ionomer cements (Nano-Ag-GIC) [J]. J Dent, 2018, 69:102-109.
[4] 刘莉霞,陈琳.玻璃离子水门汀加入二氧化钛纳米颗粒后的机械与抑菌性能[J].中国组织工程研究,2014,18(30):4838-4844.
[5] Anusha Thampi VV, Prabhu M, Kavitha K, et al. Hydroxyapatite; alumina/zirconia; and nano-bioactive glass cement for tooth-restoring applications [J]. Ceram Int, 2014, 40(9; Part A) :14355-14365.
[6] Ab Rahman I, Ghazali NAM, Bakar WZ, et al. Modification of glass ionomer cement by incorporating nanozirconia-hydroxyapatite-silica nano-powder composite by the one-pot technique for hardness and aesthetics improvement [J]. Ceram Int, 2017, 43(16): 13247-13253.
[7] Boyd D, Towler MR. The processing; mechanical properties and bioactivity of zinc based glass ionomer cements [J]. J Mater Sci Mater Med, 2005, 16(9):843-850.
[8] Silva RM, Pereira FV, Mota FA, et al. Dental glass ionomer cement reinforced by cellulose microfibers and cellulose nanocrystals [J]. Mater Sci Eng C, 2016, 58:389-395.
[9] Farooq I, Moheet IA, AlShwaimi E. In vitro dentin tubule occlusion and remineralization competence of various toothpastes [J]. Arch Oral Biol, 2015, 60(9):1246-1253.
[10] Choudhary K, Nandlal B. Comparative evaluation of shear bond strength of nano-hydroxyapatite incorporated glass ionomer cement and conventional glass ionomer cement on dense synthetic hydroxyapatite disk: An in vitro study [J]. Indian J Dent Res, 2015, 26(2):170-175.
[11] Hii SC, Luddin N, Kannan TP, et al. The biological evaluation of conventional and nano-hydroxyapatite-silica glass ionomer cement on dental pulp stem cells: A comparative study [J]. Contemp Clin Dent, 2019, 10(2):324-332.
[12] Malik S, Ahmed MA, Choudhry Z, et al. Fluoride release from glass ionomer cement containing fluoroapatite and hydroxyapatite [J]. J Ayub Med Coll Abbottabad, 2018, 30(2):198-202.
[13] Moshaverinia A, Ansari S, Moshaverinia M, et al. Effects of incorporation of hydroxyap- atite and fluoroapatite nanobioceramics into conventional glass ionomer cements (GIC) [J]. Acta Biomater, 2008, 4(2): 432-440.
[14] Sharafeddin F, Feizi N. Evaluation of the effect of adding micro-hydroxyapatite and nano-hydroxyapatite on the microleakage of conventional and resin-modified Glass-ionomer Cl V restorations [J]. J Clin Exp Dent, 2017, 9(2):e242-e248.
[15] Krishnamurithy G, Mohan S, Yahya NA, et al. The physicochemical and biomechanical profile of forsterite and its osteogenic potential of mesenchymal stromal cells [J]. PLoS One, 2019, 14(3):e0214212
[16] Sayyedan FS, Fathi MH, Edris H, et al. Effect of forsterite nanoparticles on mechanical properties of glass ionomer cements [J]. Ceram Int, 2014, 407(Part B):10743-10748.
[17] Fareed MA, Stamboulis A. Effect of nanoclay dispersion on the properties of a commercial glass ionomer cement [J]. Int J Biomater, 2014, 2014:685389.
[18] Sasaki JI, Kiba W, Abe GL, et al. Fabrication of strontium-releasable inorganic cement by incorporation of bioactive glass [J]. Dent Mater, 2019, 35(5):780-788.
[19] Garcia IM, Leitune VCB, Balbinot GS, et al. Influence of niobium pentoxide addition on the properties of glass ionomer cements [J]. Acta Biomater Odontol Scand, 2016, 2(1):138-143.
[20] Klai S, Altenburger M, Spitzmuller B, et al. Antimicrobial effects of dental luting glass ionomer cements on Streptococcus mutans [J]. ScientificWorldJournal, 2014, 2014: 807086.
[21] Mohammadi Z, Jafarzadeh H, Shalavi S. Antimicrobial efficacy of chlorhexidine as a root canal irrigant: a literature review [J]. J Oral Sci, 2014, 56(2):99-103.
[22] Yan H, Yang H, Li K, et al. Effects of chlorhexidine-encapsulated mesoporous silica nano particles on the anti-biofilm and mechanical properties of glass ionomer cement [J]. Molecules, 2017, 22(7):1225.
[23] Hook ER, Owen OJ, Bellis CA, et al. Development of a novel antimicrobial-releasing glass ionomer cement functionalized with chlorhexidine hexameta-phosphate nanoparticles [J]. J Nanobiotechnology, 2014, 12:3.
[24] Walsh T, Oliveira-Neto JM, Moore D. Chlorhexidine treatment for the prevention of dental caries in children and adolescents [J]. Cochrane Database Syst Rev, 2015, (4):CD008457.
[25] Liu SY, Tonggu L, Niu LN, et al. Antimicrobial activity of a quaternary ammonium methacryloxy silicate-containing acrylic resin: a randomised clinical trial [J]. Sci Rep, 2016, 6: 21882.
[26] Beyth N, Houri-Haddad Y, Baraness-Hadar L, et al. Surface antimicrobial activity and biocompatibility of incorporated poly-ethylenimine nanoparticles [J]. Biomaterials, 2008, 29(31):4157-4163.
[27] 黄芳,陈银燕,张瑜,等.季铵盐包裹溴化银纳米复合物改性玻璃离子水门汀的抗菌性能研究[J].牙体牙髓牙周病学杂志,2018,28(3):136-142.
[28] Mulder R, Anderson-Small C. Ion release of chitosan and nano-diamond modified glass ionomer restorative cements [J]. Clin Cosmet Investig Dent, 2019, 11:313-320.
[29] Debnath A, Kesavappa SB, Singh GP, et al. Comparative evaluation of antibacterial and adhesive properties of chitosan modified glass ionomer cement and conventional glass ionomer cement: an in vitro study [J]. J Clin Diagn Res, 2017, 11(3):ZC75-ZC78.
[30] Senthil Kumar R, Ravikumar N, Kavitha S, et al. Nanochitosan modified glass ionomer cement with enhanced mechanical properties and fluoride release [J]. Int J Biol Macromol, 2017, 104(Pt B):1860-1865.
[31] Zhou J, Xu Q, Fan C, et al. Characteristics of chitosan-modified glass ionomer cement and their effects on the adhesion and proliferation of human gingival fibroblasts: an in vitro study [J]. J Mater Sci Mater Med, 2019, 30(3):39.
[32] Sun L, Yan Z, Duan Y, et al. Improvement of the mechanical; tribological and antibacterial properties of glass ionomer cements by fluorinated graphene [J]. Dent Mater, 2018, 34(6):e115-e127.
[33] 孙兢,朱博武,杨蕾,等.纳米颗粒共掺杂对玻璃离子水门汀性能影响[J].口腔医学研究,2018,34(5):509-512.
[34] Zhang YY, Wong HM, McGrath CPJ, et al. In vitro and in vivo evaluation of electrophoresis-aided casein phosphopeptide-amorphous calcium phosphate remineralisation system on pH-cycling and acid-etching demineralised enamel [J]. Sci Rep, 2018, 8(1):8904.
[35] Zalizniak I, Palamara JE, Wong RH, et al. Ion release and physical properties of CPP-ACP modified GIC in acid solutions [J]. J Dent, 2013, 41(5):449-454.
[36] Uo M, Wada T, Asakura K. Structural analysis of strontium in human teeth treated with surface pre-reacted glass-ionomer filler eluate by using extended X-ray absorption fine structure analysis [J]. Dent Mater J, 2017, 36(2):214-221.
[37] Kim DA, Abo-Mosallam HA, Lee HY, et al. Development of a novel aluminum-free glass ionomer cement based on magnesium/strontium-silicate glasses [J]. Mater Sci Eng C Mater Biol Appl, 2014, 42:665-671.
[38] Shahid S, Hassan U, Billington RW, et al. Glass ionomer cements: Effect of strontium substitution on esthetics, radiopacity and fluoride release [J]. Dental Materials, 2014, 30(3):308-313.